产品中心 Product  >  PVC加工及抗冲击性剂 PVC processing and impact resistance agent  >  MBS系列 MBS series
MBS HI-101 低温增韧改性剂 MBS HI-101 low temperature toughening modifier
产品简介 Product Introduction
HI-101 低温增韧改性剂与CPE相比，它赋予PVC制品更高的断裂伸长率和卓越的抗冲击强度 Compared with CPE, HI-101 low-temperature toughening modifier gives PVC products higher elongation at break and excellent impact strength
产品优势 Product advantages

1.促进PVC混合料的塑化； 1. Promote the plasticization of PVC mixture;

2.卓越的断裂伸长率和韧性； 2. Excellent elongation at break and toughness;

3.低温下卓越的拉伸冲击强度； 3. Excellent tensile impact strength at low temperature;

4.良好的耐候性能； 4. Good weather resistance;

5.提高最终制品的表面光泽度 5. Improve the surface gloss of the final product

技术指标 Technical index
参数 parameter单位 unit检测标准 Testing standardCPE CPEHI-101 HI-101
外观 Exterior一 一一 一白色粉末 White powder白色粉末 White powder
表观密度 Apparent densityg/cm2 g/cm2GB/T1636-2008 GB/T1636-20080.42 0.42≥0.30 ≥0.30
筛余物（30mesh) Residue on sieve (30mesh)% %GB/T2916 GB/T29161.2 1.2≤2.0 ≤2.0
挥发分 Volatile% %ASTMD5668 ASTMD56681.12 1.121.00±0.50 1.00±0.50
性能比较 Performance comparison

1.塑化性能比较 1. Comparison of plasticizing properties

表1 测试条件 160℃，60rpm Table 1 Test conditions 160℃, 60rpm

牌号/塑化数据 Grade/Plastification Data塑化扭矩（Nm） Plasticizing torque (Nm)平衡扭矩（Nm) Balance torque (Nm)塑化时间（S） Plasticizing time (S)
0#空白基料 0#Blank base material28.9 28.928.9 28.9345 345
1#HI-101 1#HI-10134.5 34.529.1 29.1148 148
2#CPE+AIM 2#CPE+AIM34.3 34.329.1 29.1145 145

表2 测试条件 190℃，30rpm Table 2 Test conditions 190℃, 30rpm

牌号/塑化数据 Grade/Plastification Data塑化扭矩（Nm） Plasticizing torque (Nm)平衡扭矩（Nm) Balance torque (Nm)塑化时间（S） Plasticizing time (S)
0#空白基料 0#Blank base material19.0 19.017.9 17.9215 215
1#HI-101 1#HI-10124.7 24.719.9 19.984 84
2#CPE+AIM 2#CPE+AIM23.8 23.819.7 19.779 79

2.机械性能比较 2. Comparison of mechanical properties

参数/牌号 Parameters / grades单位 unit检测标准 Testing standard0#空白基料 0#Blank base material1#HI-101 1#HI-101CPE CPE
断裂伸长率 Elongation at break% %GB/T1040-92 GB/T1040-9290.8 90.8184.6 184.6152.7 152.7
简支梁冲击强度（0℃） Impact strength of simply supported beam (0℃)KJ/m2 KJ/m2GB/T1043.1-2008 GB/T1043.1-20088.6 8.614.9 14.914.7 14.7
拉伸强度 Tensile StrengthMpa MpaGB/T1040-92 GB/T1040-9245.1 45.142.2 42.242.4 42.4
硬度 hardness一 一GB/T2411-2008 GB/T2411-200883.5 83.582.4 82.482.5 82.5
维卡软化点 Vicat softening point℃ ℃GB/T1633-2000 GB/T1633-200083.2 83.282.0 82.082.3 82.3

3.抗冲击强度对比 3. Comparison of impact strength

① 拉伸冲击强度双比 ① Double ratio of tensile impact strength

拉伸冲击强度（KJ/m2) Tensile impact strength (KJ/m2)
温度 temperature23℃ 23℃0℃ 0℃一30℃ 一30℃
0#空白基料 0#Blank base material985.0 985.0574.2 574.2391.7 391.7
1#HI-101 1#HI-1011428.5 1428.5755 755661 661
2#CPE+AIM 2#CPE+AIM1032.1 1032.1630.4 630.4524.8 524.8

② 拍打冲击强度双比 ② Double ratio of impact strength

受损样本数量 Number of damaged samples
温度 temperature一5℃ 一5℃一15℃ 一15℃一25℃ 一25℃
0#空白基料 0#Blank base material4 45 56 6
1#HI-101 1#HI-1011 12 22 2
2#CPE+AIM 2#CPE+AIM2 24 45 5

备注：测试温度保持20min,24.020HZ 拍打15S;对于拍打冲击强度测试使用试验样本为6块。 Remarks: The test temperature is kept for 20min, 24.020HZ beating for 15S; for the beating impact strength test, there are 6 test samples.

4. 耐候性 4. Weather resistance

HI-101能够赋予于PVC最终制品良好的机械性能，同时展示出良好的耐候性。 HI-101 can impart good mechanical properties to the final PVC products, while exhibiting good weather resistance.

5 光泽度对比 5 Gloss comparison

测试条件：45° Test conditions: 45°

牌号 GradePVC挤出片的光泽度 The gloss of PVC extruded sheet
0#空白基料 0#Blank base material32.3 32.3
1#HI-101 1#HI-10158.9 58.9
2#CPE+AIM 2#CPE+AIM58.2 58.2

以上测试的配方 The above tested formula

成分 ingredient0# 0#1# 1#2# 2#
空白基料 Blank base materialHI-101 HI-101CPE-Y CPE-Y
PVC (K-65) PVC (K-65)100.00 100.00100.00 100.00100.00 100.00
轻质碳酸钙 Light calcium carbonate5.0 5.05.0 5.05.0 5.0
硬脂酸铅 Lead stearate1.0 1.01.0 1.01.0 1.0
硬脂酸钙 Calcium stearate0.70 0.700.70 0.700.70 0.70
二盐基亚磷酸铅 Lead Dibasic Phosphite2.50 2.502.50 2.502.50 2.50
硬脂酸 Stearic acid0.20 0.200.20 0.200.20 0.20
PE 线 PE line0.15 0.150.15 0.150.15 0.15
钛白粉 （金红石型） Titanium dioxide (rutile type)4.00 4.004.00 4.004.00 4.00
加工助剂HL-200 Processing aid HL-200一 一0.60 0.600.60 0.60
HI-101 HI-101一 一7.00 7.00一 一
CPE-Y CPE-YCPE-Y CPE-YCPE-Y CPE-Y4.00 4.00
AIM Competitor “D” AIM Competitor “D”一 一一 一3.00 3.00
产品应用 Applications

HI-101 主要应用于生产PVC户外制品。例如PVC窗型材、PVC管材和管件、PVC栅栏、PVC扣板、装饰板及PVC镶嵌板等等。 HI-101 is mainly used in the production of PVC outdoor products. For example, PVC window profiles, PVC pipes and fittings, PVC fences, PVC gussets, decorative panels and PVC inlaid panels, etc.

包装和贮藏 Packaging and storage

25kg/包，存于阴凉，干燥，无阳光直射温度低于40℃的仓库。 25kg/bag, store in a cool, dry, non-direct sunlight warehouse with temperature lower than 40℃.